MP 54110
Harmonization Code : 3214.10.00 | Putty and other mastics | Resin cements, caulking compounds and other mastics
Main features
- 1:1 Meter-Mix Dispensing
- 30-60 Minute Handling Cure
- 15.9 MPa Aluminum Shear
Product Description
H.B. Fuller MP54110 Epoxy Adhesive uses a clear, two-part unfilled epoxy system to bond metals, ceramics, and most plastics. The liquid components mix 1:1 by weight or volume and produce a typical mixed viscosity of 20,000 cP for cartridge and meter-mix-dispense application. At 25 deg C, a 20 g batch has an 8-12 minute pot life. Assemblies reach handling cure in 30-60 minutes and full cure in 24 hours at room temperature. The cured adhesive has Shore D 80 hardness, 10% elongation, and a typical operating range of -40 to 130 deg C.
Key features
- One-to-one mix ratio: Mixes 1:1 by weight or volume for cartridge or meter-mix-dispense application.
- Rapid handling cure: Reaches handling cure in 30-60 minutes at room temperature.
- Aluminum overlap shear: Provides 15.9 MPa typical overlap shear on acid-etched aluminum under ASTM D1002 conditions.
Applications / Suitable for
- Bonding metal and ceramic assemblies
- Bonding most plastic assemblies
- Cartridge or meter-mix-dispense application
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Appearance
Appearance
Clear
Chemistry Type
Chemistry Type
Epoxy
Component System
Component System
two component
Additional Information
Technical properties
Uncured and working properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Appearance | Clear liquid | As supplied | |
| Mix ratio | 1:1 | by weight or volume | Resin to hardener |
| Mixed viscosity | 20,000 | cP | Typical |
| Mixed specific gravity | 1.16 | Typical | |
| Pot life | 8-12 | min | 20 g mass at 25 deg C |
| Storage temperature | 12-25 | deg C | Unopened containers |
Technical properties
Cured properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Shore hardness | 80 | Shore D | ASTM D2240 |
| Operating temperature | -40 to 130 | deg C | Typical range |
| Overlap shear | 15.9 | MPa | ASTM D1002; acid-etched aluminum; 25 deg C; 50% RH |
| Elongation | 10 | % | Cured adhesive |